Copper slag is a by-product obtained during matte smelting and refining of copper. The common management options for copper slag are recycling, recovering of metal, production of value added products such as abrasive tools, roofing granules, cutting tools, abrasive, tiles, glass, road-base construction, railroad ballast, asphalt pavements.
strength properties of copper slag as a partial replacement of sand at different levels (0%, 20% and 40%). Copper slag is a by-product obtained during the matte smelting and refining of copper. In the present investigation it is proposed to study the engineering properties of Copper slag viz. Slump test,
proportions of copper slag replacement with sand of 0 to in concrete. It concluded that the maximum compressive strength of concrete increased by 55% at 40% replacement of fine aggregate by copper slag and flexural strength of concrete at 28 days is .
partial replacement of fine aggregate with copper slag. Addition of copper slag increases the density of concrete thereby increasing the self-weight, so that it can be used for high density concrete production. 4.9. Economic Feasibility Geopolymer concrete (GPC) manufactured using industrial waste like fly ash, GGBS and copper slag is
Experimental Investigation of Copper Slag Replacement of Fine Aggregate Ppt - Free download as Powerpoint Presentation (.ppt / .pptx), PDF File (.pdf), Text File (.txt) or view presentation slides online. Concrete Experimental investigation of copper slag replacement of fine aggregate
Copper Slag Copper slag produced during the matte smelting and refining of copper ore, during which, the iron present in the copper concentrate combines chemically at 1200°C with silica present in flux materials such as river sand/silica sand/ quartz fines to form iron silicate, which is termed as copper slag. The copper slag thus generated is ...
The results indicate that there is a slight increase in the HPC density of nearly 5% with the increase of copper slag content, whereas the workability increased rapidly with increases in copper slag percentage. Addition of up to 50% of copper slag as sand replacement yielded comparable strength with that of the control mix.
Copper slag as sand replacement The use of copper slag as sand substitution improves the strength and durability characteristics of high strength concrete up to 50% replacement level (Al-Jabri et al., 2009), increased the compressive and flexural strength of .
Addition of up to 50% of copper slag as sand replacement yielded comparable High performance concrete Copper slag strength with that of the control mix. However, further additions of copper slag caused reduction in the Waste material strength due to an increase of the free water content in the mix.
copper slag as a substitution replacement material of sand. Copper slag which is an industrial waste product can be used as replacement for cement with sand and contributes to the increase in various mechanical properties of concrete. Copper slag can be used up to 30% but when used ahead of 50% results in decrease in strengths. [13]
concrete. Partial replacement with copper slag also serves as a solution for the disposal of solid waste. REFERENCES 1. Abdullah H.AlSaidy (August 2009), "Copper slag as sand replacement for high performance concrete", Cement and Concrete Composites, 31 (7), pp 483488 19.5 20 20.5 21 21.5 0 20 40 m 2 % of Copper Slag 19.5 20 20.5 21
[6] Patil, Patil & Veshmawala observed the Performance of Copper Slag as Sand Replacement in Concrete.M30 concrete was used and various tests like compressive, flexural, split tensile strength ...
The compressive strength of cube specimen for different copper slag content as a replacement of sand at 7, 28, and 56 days curing period respectively is presented below. These results show an increasing profile up to 40% replacement of copper slag and then it shows decreasing profile as more copper slag .
copper slag can be used as a partial replacement for sand as fine aggregate in concrete up to 40% in pavement grade concrete with out any loss of cohesiveness and the compressive and flexural strength of such concretes is about 20% higher than that of conventional cement concretes of the same grade
using copper slag as a replacement of fine aggregate on the strength properties. M25 grade concrete was used and tests were conducted for various proportions of copper slag replacement with sand of 0% to in concrete. The test results indicate that compressive strength of concrete
Partial Replacement of Copper Slag as Fine Aggregate Ambrish E1, Dhavamani Doss S2, ... "Copper slag as sand replacement for high performance concrete", Cement & Concrete Composites, Vol. 31, pp. 483- 488, 2009. [2] Akihiko, Y. and Takashi, Y. "Study of utilisation of copper slag
Properties And Effects Of Copper Slag In Concrete 47 2.7 Fineness Modulus The fineness modulus of coarse aggregates (20 mm & 10 mm), sand and copper slag are 7.10, 6.77, 2.94 and 4.06 respectively. Table 3.2 to 3.3 shows the fineness modulus of 20 mm, 10 mm coarse aggregates, sand and copper slag respectively.
Aug 04, 2018· Granulated blast furnace slag ( GBFS) has been able to replace Sand to the amount of 70%. GBFS is byproduct of steel industry & hence this method is feasible at location where steel plant is located in close proximity. Copper slag is yet another r...
It is recommended that 40 wt% of copper slag can be used as replacement of sand in order to obtain HPC with good properties. 6. It should be noted that further research work is needed to explore the effect of copper slag as fine aggregates on the properties of concrete with different cement types, silica fume sources and the degree of fines.
Natural sand, as well as copper slag, was passed through 4.75 mm IS sieve. The specific gravity of natural sand and copper slag was experimentally determined to be 2.62 and 3.43, respectively, by using pycnometer as per BIS:2386 part III-1963, R 2002 . Coarse aggregates (basalt) of size 10 mm and 20 mm having a specific gravity of 2.77 and 2.82 ...
The blasting media manufactured from copper slag brings less harm to people and environment than sand. The product meets the most rigid health and ecological standards. Construction. Copper slag can be used in concrete production as a partial replacement for sand. Copper slag is used as a building material, formed into blocks.
USE OF COPPER SLAG AS A REPLACEMENT FOR FINE AGGREGATE IN CONCRETE. ... M20 grade concrete was used and tests were conducted for various proportions of copper slag replacement with sand of 0 to 60 ...
Granulated Copper Slag as a patial replacement for sand. r Fifteen concrete mixes with different proportions of Granulat-ed Copper Slag ranging from 0% (for the control mix) to were considered. All the mixes were proportioned by the method of absolute volumes considering the specific grav ity of the constituent materials.
copper slag, and also to scrutinise the following: 1. To find the optimum proportion of copper slag that can be gained maximum strength and that proportion will be used as a replacement substitute material for fine aggregate in concrete. 2. To debrief the physical and chemical properties by use of copper slag for fine aggregate in concrete